Zirconia is a material with high mechanical strength and fracture toughness at room temperature. Our zirconia (ZrO2) is added with 3mol%Y2O3 partial stable zirconia (PSZ). Because the particle diameter of PSZ material is small, it can be processed with high precision, and its application in precision machining parts such as molds is expanding. In addition, can also be used for industrial tools, optical connector parts and crushing equipment medium. The high fracture toughness of PSZ can be used to make special springs, and it is also widely used in domestic ceramic knives, slicer and other parts.
Zirconia (ZrO2) I main uses
Mold and mould tools (various molds, precision positioning fixture, insulation fixture); Mill parts (classifier, air flow mill, bead mill); Industrial tool (industrial cutter, slitter machine, flat press roll); Optical connector components (sealing ring, sleeve, V-groove fixture); Special spring (coil spring, plate spring); Consumer products (small insulated screwdriver, ceramic knife, slicer).
Material Properties
| Item | 95% Alumina | 99% Alumina | Zirconia | Silicon carbide | Silicon Nitride | Aluminum Nitride | Machinable ceramic |
| Colour | white | Light yellow | white | black | black | gray | white |
| Density (g/cm3) | 3.7g/cm3 | 3.9g/cm3 | 6.02g/cm3 | 3.2g/cm3 | 3.25g/cm3 | 3.2g/cm3 | 2.48g/cm3 |
| Water Absorption | 0% | 0% | 0% | 0% | 0% | 0% | 0% |
| Hardness(HV) | 23.7 | 23.7 | 16.5 | 33 | 20 | - | - |
| Flexural Strength(MPa) | 300MPa | 400MPa | 1100MPa | 450MPa | 800MPa | 310MPa | 91MPa |
| Compressive Strength(MPa) | 2500MPa | 2800MPa | 3600MPa | 2000MPa | 2600MPa | - | 340MPa |
| Young's Modulus Of Elasticity | 300GPa | 300GPa | 320GPa | 450GPa | 290GPa | 310~350GPa | 65GPa |
| Poisson's Ratio | 0.23 | 0.23 | 0.25 | 0.14 | 0.24 | 0.24 | 0.29 |
| Thermal Conductivity | 20W/m°C | 32W/m°C | 3W/m°C | 50W/m°C | 25W/m°C | 150W/m°C | 1.46W/m°C |
| Dielectric Strength | 14KV/mm | 14KV/mm | 14KV/mm | 14KV/mm | 14KV/mm | 14KV/mm | 14KV/mm |
| Volume Resistivity(25℃) | >1014Ω·cm | >1014Ω·cm | >1014Ω·cm | >105Ω·cm | >1014Ω·cm | >1014Ω·cm | >1014Ω·cm |